EPOXY ASPHALT BINDER FOR WEAR-RESISTANT ROAD SURFACING
PRODUCT OVERVIEW
High grade roads such as freeways are normally multi-layered structures. The surface layer directly affects the durability of the underlying structure. Epoxy asphalt polymer concrete with its excellent wear resistance is becoming more widely used for wear-resistant veneers in high-grade highway construction. Following are the main features:
■ Dual functional groups epoxy asphalt
■ Good high / low temperature resistance
■ Excellent anti-wear and fatigue resistance
■ Water proof, anti-corrosion, high strength
APPLICATIONS
COOLBOND® EP-307 is an Epoxy Asphalt polymer concrete binder suitable for cold mixing processes. The product is designed to have medium pot life for large area of paving works.
EP-307 is a formulated product based on dual functional liquid epoxy asphalt resins to have good wear resistance and excellent heat stability in a wide range of temperatures.
PRODUCTS
APPLICATION GUIDE
1. Mix Part A and Part B of the product at a ratio of 1.5 (A): 1 (B)
2. Apply the mixture to the designated area immediately.
3. Spread the mixture evenly and avoid air bubbles from occurring
4. The mixture must be used up within its recommended pot life.
5. Clean up the unused products.
TECHNICAL PARAMETERS
Product Name | Appearance | Viscosity (25ºC, CPS) | Curing Time (min) | Initial Curing Time (25ºC, min) | Mix Ratio A:B RATIO |
EP-307A | Black viscous liquid | 7000-8000 | 1.5 | 100 – 120 | 5– 6 |
EP-307B | Black viscous liquid | 6000–8000 | 1 |
|
|
Physical Properties (Fully Cured Product) | Ratio:A :B = 1.5 :1 | Standards | |
Test Result | |||
Tensile Strength,Mpa | 4.5 | GB/T2569-1995 | |
Elongation strength,Mpa | 185 | GB/T2568-1995 | |
Hardness (Shore D) | 35 | GB/T51-1999 | |
Marshall stability(KN) | 23.7 | JTJ E20-2011/T0709-2011 | |
Anti-rutting dynamic stability (times / mm) | >70000 | JTJ E20-2011/T0719-2011 | |
|
|
|
|
APPLICATION CASES
EPOXY ASPHALT BINDER FOR WEAR-RESISTANT ROAD SURFACING
PRODUCT OVERVIEW
High grade roads such as freeways are normally multi-layered structures. The surface layer directly affects the durability of the underlying structure. Epoxy asphalt polymer concrete with its excellent wear resistance is becoming more widely used for wear-resistant veneers in high-grade highway construction. Following are the main features:
■ Dual functional groups epoxy asphalt
■ Good high / low temperature resistance
■ Excellent anti-wear and fatigue resistance
■ Water proof, anti-corrosion, high strength
APPLICATIONS
COOLBOND® EP-307 is an Epoxy Asphalt polymer concrete binder suitable for cold mixing processes. The product is designed to have medium pot life for large area of paving works.
EP-307 is a formulated product based on dual functional liquid epoxy asphalt resins to have good wear resistance and excellent heat stability in a wide range of temperatures.
PRODUCTS
APPLICATION GUIDE
1. Mix Part A and Part B of the product at a ratio of 1.5 (A): 1 (B)
2. Apply the mixture to the designated area immediately.
3. Spread the mixture evenly and avoid air bubbles from occurring
4. The mixture must be used up within its recommended pot life.
5. Clean up the unused products.
TECHNICAL PARAMETERS
Product Name | Appearance | Viscosity (25ºC, CPS) | Curing Time (min) | Initial Curing Time (25ºC, min) | Mix Ratio A:B RATIO |
EP-307A | Black viscous liquid | 7000-8000 | 1.5 | 100 – 120 | 5– 6 |
EP-307B | Black viscous liquid | 6000–8000 | 1 |
|
|
Physical Properties (Fully Cured Product) | Ratio:A :B = 1.5 :1 | Standards | |
Test Result | |||
Tensile Strength,Mpa | 4.5 | GB/T2569-1995 | |
Elongation strength,Mpa | 185 | GB/T2568-1995 | |
Hardness (Shore D) | 35 | GB/T51-1999 | |
Marshall stability(KN) | 23.7 | JTJ E20-2011/T0709-2011 | |
Anti-rutting dynamic stability (times / mm) | >70000 | JTJ E20-2011/T0719-2011 | |
|
|
|
|